Dynamics of Gold Droplet Formation on SiO 2 /Si(111) Surface - Université Clermont Auvergne Access content directly
Journal Articles Journal of Physical Chemistry C Year : 2020

Dynamics of Gold Droplet Formation on SiO 2 /Si(111) Surface

Guillaume Monier
Gabin Grégoire
  • Function : Author
Evelyne Gil
Vladimir G Dubrovskii
Christine Robert-Goumet


Au droplets are used as a catalyst for the growth of nanowires on Si(111) substrate via the vapor-liquid-solid (VLS) mechanism. The dewetting of a Au thin film is the most common method to obtain these droplets. The control of this step is crucial to adjust the density and the diameter of the nanowires during VLS growth. When the Si(111) substrate is covered with a silicon dioxide layer, the kinetics of Au droplet formation is strongly modified. The dependence of the diameter and spatial distribution of the droplets on the surface have been studied by scanning electron microscopy with respect to the thickness of the silicon dioxide layer, the thickness of the Au film and the temperature of the substrate during deposition and post-deposition annealing. In-situ low energy electron microscopy and low energy electron diffraction revealed the dynamics of the Au droplet formation after annealing. The Au droplets are shown to catalyze the decomposition of silicon dioxide at high temperature (> 650-700 °C) and form a wetting layer of Au-(33)-Si(111). Consequently, the droplets absorb silicon atoms from the substrate, migrate perpendicular to the atomic steps and grow by the Smoluchowski ripening process.
Fichier principal
Vignette du fichier
Dynamics of Au droplet formation on SiO2Si(111) surface.pdf (6.87 Mo) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-02992036 , version 1 (06-11-2020)



Hadi Hijazi, Frédéric Leroy, Guillaume Monier, Gabin Grégoire, Evelyne Gil, et al.. Dynamics of Gold Droplet Formation on SiO 2 /Si(111) Surface. Journal of Physical Chemistry C, 2020, 124 (22), pp.11946-11951. ⟨10.1021/acs.jpcc.0c02378⟩. ⟨hal-02992036⟩
69 View
266 Download



Gmail Facebook X LinkedIn More