Influence of water vapour on 316L oxidation at high temperature - in situ X-Ray diffraction
Influence de la vapeur d’eau sur l’oxydation haute température d’un acier 316L – Étude par diffraction de RX in situ
Résumé
Water vapour mixed with air (10 vol.% H 2 O) has little effect on the AISI 316L stainless steel oxidation under isothermal conditions at 800 and 900 °C. The oxide scale is composed of Cr 2 O 3 and Mn 1.5 Cr 1.5 O 4 located at the external interface. Results show that the presence of water lowers the specimen's mass gain. At 1000 °C, the effect of water vapour on the scale structure is deleterious. In situ X-ray diffraction permits to show that the breakaway is due to iron oxidation starting after about 30 hours. This leads to an external Fe 2 O 3 scale growth and an internal multilayered FeCr 2 O 4 scale formation.
L’air contenant 10 vol.% H2O a peu d’effet sur l’oxydation de l’alliage AISI 316L à 800 et 900°C. La couche d’oxyde est alors constituée de Cr2O3 et de Mn1.5Cr1.5O4 qui est situé à l’interface externe. Les résultats montrent que la présence de vapeur d’eau diminue la vitesse de prise de masse. A 1000 °C la vapeur d’eau a un effet désastreux sur la structure de la couche d’oxyde. La diffraction des rayons X in situ à 1000°C sous air humide a permis de montrer que l’oxydation du fer débute après environ 30 heures d’oxydation. Ceci conduit à la formation d’une couche externe de Fe2O3 et une couche interne stratifiée de FeCr2O4.
Fichier principal
ARTICLE Henri BUSCAIL 316L H2O (ACSM) 2015 Article (Corrigé).pdf (1.73 Mo)
Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...