Influence of Lanthanum Coatings on a Model 330 Alloy (Fe–35Ni–18Cr–2Si) Oxidation at High Temperatures

Résumé

The influence of a lanthanum sol-gel coating on the chromia scale adherence has been studied on the 330 alloy (Fe-35Ni-18Cr-2Si) oxidized at 900°C, in air. Argon annealing of lanthanum sol-gel coatings have been performed at various temperatures. Kinetic results show that lanthanum sol-gel coatings lead to a lower oxidation rate compared to blank specimens. On blank 330 specimens scale spallation is observed after cooling to room temperature. On the non-annealed sol-gel coated specimen and the argon annealed specimens at 600, 800 or 1000°C, the oxide scale formed at 900 °C is adherent after 48 hours isothermal oxidation. The adherent oxide scales are convoluted. It results from o an anionic and a cationic mixed diffusion process in the chromia scale Thermal cycling tests on lanthanum the sol-gel coated specimen show that the oxide scale remains adherent after 250 cycles. It is concluded that argon annealing of the lanthanum sol gel coating is not necessary to improve the scale adherence.
Fichier principal
Vignette du fichier
Art HB (2014) Oxid Met (330 + Lanthane) 2013 05 12.pdf (953.21 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01628272 , version 1 (03-11-2017)

Identifiants

Citer

Henri Buscail, Christophe Issartel, Frédéric Riffard, Raphaël Rolland, Sébastien Perrier, et al.. Influence of Lanthanum Coatings on a Model 330 Alloy (Fe–35Ni–18Cr–2Si) Oxidation at High Temperatures. Oxidation of Metals, 2014, 81 (1-2), pp.127-138. ⟨10.1007/s11085-013-9423-x⟩. ⟨hal-01628272⟩

Collections

PRES_CLERMONT
86 Consultations
199 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More